Base-resistant adsorbents prepared using diamino group-grafted mesoporous silica uniformly coated with zirconia

Masaki Okamoto, Haruka Satake, Hiroyuki Seki

Research output: Contribution to journalArticle

3 Citations (Scopus)

Abstract

The mesopore walls of ordered mesoporous silicas were coated with zirconia layers at room temperature using zirconia tetra-n-butoxide dissolved in dry toluene. It was found that coating the silicas three times with zirconia layers was sufficient to completely cover their pore walls with zirconia. The coated mesoporous silicas demonstrated high resistance to a 2 M sodium hydroxide solution at 0 °C. Prior to being coated three times with the zirconia layers, the silica walls were partially coated with 3-(2-aminoethylamino)propyltrimethoxysilane so that diamino groups could be grafted onto the pore walls; this was done so that they could be used as base-resistant adsorbents for copper(ii) ions that had been dissolved in basic solutions. The grafted diamino groups, which captured copper(ii) ions, were protected from the basic solution, as the silyl in the diamino groups was covered with zirconia layers.

Original languageEnglish
Pages (from-to)24425-24432
Number of pages8
JournalJournal of Materials Chemistry A
Volume5
Issue number46
DOIs
Publication statusPublished - 2017 Jan 1
Externally publishedYes

Fingerprint

Silicon Dioxide
Zirconia
Adsorbents
Silica
Copper
Ions
Sodium Hydroxide
Toluene
zirconium oxide
Sodium
Coatings
Temperature

ASJC Scopus subject areas

  • Chemistry(all)
  • Renewable Energy, Sustainability and the Environment
  • Materials Science(all)

Cite this

Base-resistant adsorbents prepared using diamino group-grafted mesoporous silica uniformly coated with zirconia. / Okamoto, Masaki; Satake, Haruka; Seki, Hiroyuki.

In: Journal of Materials Chemistry A, Vol. 5, No. 46, 01.01.2017, p. 24425-24432.

Research output: Contribution to journalArticle

@article{3cfd47639cc84907a7d14a1f6e38de79,
title = "Base-resistant adsorbents prepared using diamino group-grafted mesoporous silica uniformly coated with zirconia",
abstract = "The mesopore walls of ordered mesoporous silicas were coated with zirconia layers at room temperature using zirconia tetra-n-butoxide dissolved in dry toluene. It was found that coating the silicas three times with zirconia layers was sufficient to completely cover their pore walls with zirconia. The coated mesoporous silicas demonstrated high resistance to a 2 M sodium hydroxide solution at 0 °C. Prior to being coated three times with the zirconia layers, the silica walls were partially coated with 3-(2-aminoethylamino)propyltrimethoxysilane so that diamino groups could be grafted onto the pore walls; this was done so that they could be used as base-resistant adsorbents for copper(ii) ions that had been dissolved in basic solutions. The grafted diamino groups, which captured copper(ii) ions, were protected from the basic solution, as the silyl in the diamino groups was covered with zirconia layers.",
author = "Masaki Okamoto and Haruka Satake and Hiroyuki Seki",
year = "2017",
month = "1",
day = "1",
doi = "10.1039/c7ta08328a",
language = "English",
volume = "5",
pages = "24425--24432",
journal = "Journal of Materials Chemistry A",
issn = "2050-7488",
publisher = "Royal Society of Chemistry",
number = "46",

}

TY - JOUR

T1 - Base-resistant adsorbents prepared using diamino group-grafted mesoporous silica uniformly coated with zirconia

AU - Okamoto, Masaki

AU - Satake, Haruka

AU - Seki, Hiroyuki

PY - 2017/1/1

Y1 - 2017/1/1

N2 - The mesopore walls of ordered mesoporous silicas were coated with zirconia layers at room temperature using zirconia tetra-n-butoxide dissolved in dry toluene. It was found that coating the silicas three times with zirconia layers was sufficient to completely cover their pore walls with zirconia. The coated mesoporous silicas demonstrated high resistance to a 2 M sodium hydroxide solution at 0 °C. Prior to being coated three times with the zirconia layers, the silica walls were partially coated with 3-(2-aminoethylamino)propyltrimethoxysilane so that diamino groups could be grafted onto the pore walls; this was done so that they could be used as base-resistant adsorbents for copper(ii) ions that had been dissolved in basic solutions. The grafted diamino groups, which captured copper(ii) ions, were protected from the basic solution, as the silyl in the diamino groups was covered with zirconia layers.

AB - The mesopore walls of ordered mesoporous silicas were coated with zirconia layers at room temperature using zirconia tetra-n-butoxide dissolved in dry toluene. It was found that coating the silicas three times with zirconia layers was sufficient to completely cover their pore walls with zirconia. The coated mesoporous silicas demonstrated high resistance to a 2 M sodium hydroxide solution at 0 °C. Prior to being coated three times with the zirconia layers, the silica walls were partially coated with 3-(2-aminoethylamino)propyltrimethoxysilane so that diamino groups could be grafted onto the pore walls; this was done so that they could be used as base-resistant adsorbents for copper(ii) ions that had been dissolved in basic solutions. The grafted diamino groups, which captured copper(ii) ions, were protected from the basic solution, as the silyl in the diamino groups was covered with zirconia layers.

UR - http://www.scopus.com/inward/record.url?scp=85036450878&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=85036450878&partnerID=8YFLogxK

U2 - 10.1039/c7ta08328a

DO - 10.1039/c7ta08328a

M3 - Article

AN - SCOPUS:85036450878

VL - 5

SP - 24425

EP - 24432

JO - Journal of Materials Chemistry A

JF - Journal of Materials Chemistry A

SN - 2050-7488

IS - 46

ER -