Densification behavior of calcium phosphates on spark plasma sintering

Daisuke Kawagoe, Yoshihiro Koga, Noriko Kotobuki, Hajime Ohgushi, Emile Hideki Ishida, Koji Ioku

Research output: Contribution to journalArticle

2 Citations (Scopus)

Abstract

Ceramics of hydroxyapatite (Ca10(PO4)6 (OH)2: HA) and β-tricalcium phosphate (β-Ca 3(PO4)2: β-TCP), were prepared by spark plasma sintering (SPS) at the temperatures from 800°C to 1000°C for 10 min with a heating rate of 25°C·min-1. The HA ceramics prepared at 900°C and 1000°C showed transparency. On the other hands, transparent β-TCP ceramics was obtained by SPS at 1000°C. In analysis of the densification behavior during sintering of HA and β-TCP by SPS, dominant sintering mechanism was plastic flow in the early stage of densification. Transparent ceramics should be the most suitable materilas to investigate the interface between human cells and ceramics.

Original languageEnglish
Pages (from-to)171-174
Number of pages4
JournalKey Engineering Materials
Volume309-311 I
Publication statusPublished - 2006
Externally publishedYes

Fingerprint

Calcium Phosphates
Spark plasma sintering
Calcium phosphate
Densification
Sintering
Durapatite
Heating rate
Plastic flow
Hydroxyapatite
Transparency
Phosphates
Cells
Temperature

Keywords

  • β-Tricalcium Phosphate
  • Hydroxyapatite
  • Spark Plasma Sintering
  • Transparency

ASJC Scopus subject areas

  • Ceramics and Composites
  • Chemical Engineering (miscellaneous)

Cite this

Kawagoe, D., Koga, Y., Kotobuki, N., Ohgushi, H., Ishida, E. H., & Ioku, K. (2006). Densification behavior of calcium phosphates on spark plasma sintering. Key Engineering Materials, 309-311 I, 171-174.

Densification behavior of calcium phosphates on spark plasma sintering. / Kawagoe, Daisuke; Koga, Yoshihiro; Kotobuki, Noriko; Ohgushi, Hajime; Ishida, Emile Hideki; Ioku, Koji.

In: Key Engineering Materials, Vol. 309-311 I, 2006, p. 171-174.

Research output: Contribution to journalArticle

Kawagoe, D, Koga, Y, Kotobuki, N, Ohgushi, H, Ishida, EH & Ioku, K 2006, 'Densification behavior of calcium phosphates on spark plasma sintering', Key Engineering Materials, vol. 309-311 I, pp. 171-174.
Kawagoe D, Koga Y, Kotobuki N, Ohgushi H, Ishida EH, Ioku K. Densification behavior of calcium phosphates on spark plasma sintering. Key Engineering Materials. 2006;309-311 I:171-174.
Kawagoe, Daisuke ; Koga, Yoshihiro ; Kotobuki, Noriko ; Ohgushi, Hajime ; Ishida, Emile Hideki ; Ioku, Koji. / Densification behavior of calcium phosphates on spark plasma sintering. In: Key Engineering Materials. 2006 ; Vol. 309-311 I. pp. 171-174.
@article{eb4fc610d7fe48fa9bf125c8209a6d24,
title = "Densification behavior of calcium phosphates on spark plasma sintering",
abstract = "Ceramics of hydroxyapatite (Ca10(PO4)6 (OH)2: HA) and β-tricalcium phosphate (β-Ca 3(PO4)2: β-TCP), were prepared by spark plasma sintering (SPS) at the temperatures from 800°C to 1000°C for 10 min with a heating rate of 25°C·min-1. The HA ceramics prepared at 900°C and 1000°C showed transparency. On the other hands, transparent β-TCP ceramics was obtained by SPS at 1000°C. In analysis of the densification behavior during sintering of HA and β-TCP by SPS, dominant sintering mechanism was plastic flow in the early stage of densification. Transparent ceramics should be the most suitable materilas to investigate the interface between human cells and ceramics.",
keywords = "β-Tricalcium Phosphate, Hydroxyapatite, Spark Plasma Sintering, Transparency",
author = "Daisuke Kawagoe and Yoshihiro Koga and Noriko Kotobuki and Hajime Ohgushi and Ishida, {Emile Hideki} and Koji Ioku",
year = "2006",
language = "English",
volume = "309-311 I",
pages = "171--174",
journal = "Key Engineering Materials",
issn = "1013-9826",
publisher = "Trans Tech Publications",

}

TY - JOUR

T1 - Densification behavior of calcium phosphates on spark plasma sintering

AU - Kawagoe, Daisuke

AU - Koga, Yoshihiro

AU - Kotobuki, Noriko

AU - Ohgushi, Hajime

AU - Ishida, Emile Hideki

AU - Ioku, Koji

PY - 2006

Y1 - 2006

N2 - Ceramics of hydroxyapatite (Ca10(PO4)6 (OH)2: HA) and β-tricalcium phosphate (β-Ca 3(PO4)2: β-TCP), were prepared by spark plasma sintering (SPS) at the temperatures from 800°C to 1000°C for 10 min with a heating rate of 25°C·min-1. The HA ceramics prepared at 900°C and 1000°C showed transparency. On the other hands, transparent β-TCP ceramics was obtained by SPS at 1000°C. In analysis of the densification behavior during sintering of HA and β-TCP by SPS, dominant sintering mechanism was plastic flow in the early stage of densification. Transparent ceramics should be the most suitable materilas to investigate the interface between human cells and ceramics.

AB - Ceramics of hydroxyapatite (Ca10(PO4)6 (OH)2: HA) and β-tricalcium phosphate (β-Ca 3(PO4)2: β-TCP), were prepared by spark plasma sintering (SPS) at the temperatures from 800°C to 1000°C for 10 min with a heating rate of 25°C·min-1. The HA ceramics prepared at 900°C and 1000°C showed transparency. On the other hands, transparent β-TCP ceramics was obtained by SPS at 1000°C. In analysis of the densification behavior during sintering of HA and β-TCP by SPS, dominant sintering mechanism was plastic flow in the early stage of densification. Transparent ceramics should be the most suitable materilas to investigate the interface between human cells and ceramics.

KW - β-Tricalcium Phosphate

KW - Hydroxyapatite

KW - Spark Plasma Sintering

KW - Transparency

UR - http://www.scopus.com/inward/record.url?scp=33645453946&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=33645453946&partnerID=8YFLogxK

M3 - Article

VL - 309-311 I

SP - 171

EP - 174

JO - Key Engineering Materials

JF - Key Engineering Materials

SN - 1013-9826

ER -