Determination of tensile properties and residual stresses of Ni-Co thin films

Jun Hyub Park, Hong Yeol Bae, Yun Jae Kim

Research output: Contribution to journalArticle

5 Citations (Scopus)

Abstract

This paper reports tensile properties and residual stresses of Ni-Co thin films. To measure elastic (and plastic) properties, direct tensile tests using dog-bone type specimens are performed first. Assuming that residual stresses vary linearly through the film thickness, bending and membrane residual stress components are measured using cantilever beam and T-structure beam specimens, respectively. Averaged values of Young's modulus, yield strength and tensile strength are found to be about 163GPa, 1,700MPa and 2,000MPa, respectively. The membrane and bending residual stress components are found to be about 825MPa and 47MPa, respectively.

Original languageEnglish
Pages (from-to)771-778
Number of pages8
JournalInternational Journal of Precision Engineering and Manufacturing
Volume11
Issue number5
DOIs
Publication statusPublished - 2010 Oct 1
Externally publishedYes

Fingerprint

Tensile properties
Residual stresses
Thin films
Membranes
Cantilever beams
Yield stress
Film thickness
Bone
Tensile strength
Elastic moduli
Plastics

Keywords

  • Finite element analysis
  • Ni-co thin film
  • Residual stress measurement
  • Tensile properties measurement

ASJC Scopus subject areas

  • Mechanical Engineering
  • Industrial and Manufacturing Engineering
  • Electrical and Electronic Engineering

Cite this

Determination of tensile properties and residual stresses of Ni-Co thin films. / Park, Jun Hyub; Bae, Hong Yeol; Kim, Yun Jae.

In: International Journal of Precision Engineering and Manufacturing, Vol. 11, No. 5, 01.10.2010, p. 771-778.

Research output: Contribution to journalArticle

@article{1dec1252f68c4703900569382cc2cc20,
title = "Determination of tensile properties and residual stresses of Ni-Co thin films",
abstract = "This paper reports tensile properties and residual stresses of Ni-Co thin films. To measure elastic (and plastic) properties, direct tensile tests using dog-bone type specimens are performed first. Assuming that residual stresses vary linearly through the film thickness, bending and membrane residual stress components are measured using cantilever beam and T-structure beam specimens, respectively. Averaged values of Young's modulus, yield strength and tensile strength are found to be about 163GPa, 1,700MPa and 2,000MPa, respectively. The membrane and bending residual stress components are found to be about 825MPa and 47MPa, respectively.",
keywords = "Finite element analysis, Ni-co thin film, Residual stress measurement, Tensile properties measurement",
author = "Park, {Jun Hyub} and Bae, {Hong Yeol} and Kim, {Yun Jae}",
year = "2010",
month = "10",
day = "1",
doi = "10.1007/s12541-010-0091-3",
language = "English",
volume = "11",
pages = "771--778",
journal = "International Journal of Precision Engineering and Manufacturing",
issn = "2234-7593",
publisher = "Korean Society of Precision Engineering",
number = "5",

}

TY - JOUR

T1 - Determination of tensile properties and residual stresses of Ni-Co thin films

AU - Park, Jun Hyub

AU - Bae, Hong Yeol

AU - Kim, Yun Jae

PY - 2010/10/1

Y1 - 2010/10/1

N2 - This paper reports tensile properties and residual stresses of Ni-Co thin films. To measure elastic (and plastic) properties, direct tensile tests using dog-bone type specimens are performed first. Assuming that residual stresses vary linearly through the film thickness, bending and membrane residual stress components are measured using cantilever beam and T-structure beam specimens, respectively. Averaged values of Young's modulus, yield strength and tensile strength are found to be about 163GPa, 1,700MPa and 2,000MPa, respectively. The membrane and bending residual stress components are found to be about 825MPa and 47MPa, respectively.

AB - This paper reports tensile properties and residual stresses of Ni-Co thin films. To measure elastic (and plastic) properties, direct tensile tests using dog-bone type specimens are performed first. Assuming that residual stresses vary linearly through the film thickness, bending and membrane residual stress components are measured using cantilever beam and T-structure beam specimens, respectively. Averaged values of Young's modulus, yield strength and tensile strength are found to be about 163GPa, 1,700MPa and 2,000MPa, respectively. The membrane and bending residual stress components are found to be about 825MPa and 47MPa, respectively.

KW - Finite element analysis

KW - Ni-co thin film

KW - Residual stress measurement

KW - Tensile properties measurement

UR - http://www.scopus.com/inward/record.url?scp=78049364106&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=78049364106&partnerID=8YFLogxK

U2 - 10.1007/s12541-010-0091-3

DO - 10.1007/s12541-010-0091-3

M3 - Article

VL - 11

SP - 771

EP - 778

JO - International Journal of Precision Engineering and Manufacturing

JF - International Journal of Precision Engineering and Manufacturing

SN - 2234-7593

IS - 5

ER -