Development of IH-FPP processing system by induction heating and surface modification of S45C steel

Atsushi Sasago, Shoichi Kikuchi, Yutaka Kameyama, Jun Komotori, Kengo Fukazawa, Yoshitaka Misaka, Kazuhiro Kawasaki

Research output: Contribution to journalArticle

17 Citations (Scopus)

Abstract

A new surface treatment system (IH-FPPsystem) combined with an induction heating and a fine particle peening machine were developed. FPP treatments were carried out on structural steel discs by using Cr shot particle at room temperature, 400°C, 600°C and 900°C. After characterizing the surfaces by SEM, EDX and XRD, corrosion tests were performed by a three electrode method using a computer driven potentiostat. No noticeable differences were observed on the specimen treated at RT, 400°C and 600°C. In the case of the specimen treated at 900°C, however, higher corrosion resistance which is almost the same as FPP treated stainless steel (SUS316L) was observed. This was because Cr diffused layer covered with relatively smooth oxidized surface prevented a corrosion reaction in 3%NaCl environment.

Original languageEnglish
Pages (from-to)347-352
Number of pages6
JournalNippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals
Volume72
Issue number5
DOIs
Publication statusPublished - 2008 May

Fingerprint

induction heating
Induction heating
Steel
Surface treatment
steels
Corrosion
peening
corrosion tests
Shot peening
Stainless Steel
Processing
surface treatment
corrosion resistance
shot
Corrosion resistance
Energy dispersive spectroscopy
stainless steels
corrosion
Stainless steel
Scanning electron microscopy

Keywords

  • Corrosion
  • Fine particle peening
  • IH-FPP system
  • Induction heating
  • Surface modification

ASJC Scopus subject areas

  • Metals and Alloys

Cite this

Development of IH-FPP processing system by induction heating and surface modification of S45C steel. / Sasago, Atsushi; Kikuchi, Shoichi; Kameyama, Yutaka; Komotori, Jun; Fukazawa, Kengo; Misaka, Yoshitaka; Kawasaki, Kazuhiro.

In: Nippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals, Vol. 72, No. 5, 05.2008, p. 347-352.

Research output: Contribution to journalArticle

Sasago, Atsushi ; Kikuchi, Shoichi ; Kameyama, Yutaka ; Komotori, Jun ; Fukazawa, Kengo ; Misaka, Yoshitaka ; Kawasaki, Kazuhiro. / Development of IH-FPP processing system by induction heating and surface modification of S45C steel. In: Nippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals. 2008 ; Vol. 72, No. 5. pp. 347-352.
@article{a08c1120dc864dcd8556bc1346d1e6d5,
title = "Development of IH-FPP processing system by induction heating and surface modification of S45C steel",
abstract = "A new surface treatment system (IH-FPPsystem) combined with an induction heating and a fine particle peening machine were developed. FPP treatments were carried out on structural steel discs by using Cr shot particle at room temperature, 400°C, 600°C and 900°C. After characterizing the surfaces by SEM, EDX and XRD, corrosion tests were performed by a three electrode method using a computer driven potentiostat. No noticeable differences were observed on the specimen treated at RT, 400°C and 600°C. In the case of the specimen treated at 900°C, however, higher corrosion resistance which is almost the same as FPP treated stainless steel (SUS316L) was observed. This was because Cr diffused layer covered with relatively smooth oxidized surface prevented a corrosion reaction in 3{\%}NaCl environment.",
keywords = "Corrosion, Fine particle peening, IH-FPP system, Induction heating, Surface modification",
author = "Atsushi Sasago and Shoichi Kikuchi and Yutaka Kameyama and Jun Komotori and Kengo Fukazawa and Yoshitaka Misaka and Kazuhiro Kawasaki",
year = "2008",
month = "5",
doi = "10.2320/jinstmet.72.347",
language = "English",
volume = "72",
pages = "347--352",
journal = "Nippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals",
issn = "0021-4876",
publisher = "Japan Institute of Metals (JIM)",
number = "5",

}

TY - JOUR

T1 - Development of IH-FPP processing system by induction heating and surface modification of S45C steel

AU - Sasago, Atsushi

AU - Kikuchi, Shoichi

AU - Kameyama, Yutaka

AU - Komotori, Jun

AU - Fukazawa, Kengo

AU - Misaka, Yoshitaka

AU - Kawasaki, Kazuhiro

PY - 2008/5

Y1 - 2008/5

N2 - A new surface treatment system (IH-FPPsystem) combined with an induction heating and a fine particle peening machine were developed. FPP treatments were carried out on structural steel discs by using Cr shot particle at room temperature, 400°C, 600°C and 900°C. After characterizing the surfaces by SEM, EDX and XRD, corrosion tests were performed by a three electrode method using a computer driven potentiostat. No noticeable differences were observed on the specimen treated at RT, 400°C and 600°C. In the case of the specimen treated at 900°C, however, higher corrosion resistance which is almost the same as FPP treated stainless steel (SUS316L) was observed. This was because Cr diffused layer covered with relatively smooth oxidized surface prevented a corrosion reaction in 3%NaCl environment.

AB - A new surface treatment system (IH-FPPsystem) combined with an induction heating and a fine particle peening machine were developed. FPP treatments were carried out on structural steel discs by using Cr shot particle at room temperature, 400°C, 600°C and 900°C. After characterizing the surfaces by SEM, EDX and XRD, corrosion tests were performed by a three electrode method using a computer driven potentiostat. No noticeable differences were observed on the specimen treated at RT, 400°C and 600°C. In the case of the specimen treated at 900°C, however, higher corrosion resistance which is almost the same as FPP treated stainless steel (SUS316L) was observed. This was because Cr diffused layer covered with relatively smooth oxidized surface prevented a corrosion reaction in 3%NaCl environment.

KW - Corrosion

KW - Fine particle peening

KW - IH-FPP system

KW - Induction heating

KW - Surface modification

UR - http://www.scopus.com/inward/record.url?scp=46649096659&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=46649096659&partnerID=8YFLogxK

U2 - 10.2320/jinstmet.72.347

DO - 10.2320/jinstmet.72.347

M3 - Article

AN - SCOPUS:46649096659

VL - 72

SP - 347

EP - 352

JO - Nippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals

JF - Nippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals

SN - 0021-4876

IS - 5

ER -