Ductile failure analyses for API X65 pipes based on local failure criteria

Chang Kyun Oh, Yun Jae Kim, Jong Hyun Baek, Young Pyo Kim, Woo Sik Kim

Research output: Chapter in Book/Report/Conference proceedingConference contribution

5 Citations (Scopus)

Abstract

A local failure criterion for the API X65 steel is applied to predict ductile failure of full-scale API X65 pipes with simulated corrosion and gouge defects under internal pressure. The local failure criterion is the stress-modified fracture strain for the API X65 steel as a function of the stress triaxiality (defined by the ratio of the hydrostatic stress to the effective stress). Based on detailed FE analyses with the proposed local failure criteria, burst pressures of defective pipes are estimated and compared with experimental data. The Failure of corroded pipes is governed by local necking and plastic collapse in the defective region, rather than failure. For pipes with gouge defects, on the other hand, it is found that fracture is dominant. The predicted burst pressures are in good agreement with experimental data. Noting that an assessment equation against the gouge defect is not yet available, parametric study is performed, from which a simple equation is proposed to predict burst pressure for API X65 pipes with gouge defects.

Original languageEnglish
Title of host publicationProceedings of 2006 ASME Pressure Vessels and Piping Division Conference - ASME PVP2006/ICPVT-11 Conference - Pressure Vessel Technologies for the Global Community
DOIs
Publication statusPublished - 2006 Nov 29
Externally publishedYes
EventASME PVP2006/ICPVT-11 Conference - Vancouver, BC, Canada
Duration: 2006 Jul 232006 Jul 27

Publication series

NameAmerican Society of Mechanical Engineers, Pressure Vessels and Piping Division (Publication) PVP
Volume2006
ISSN (Print)0277-027X

Other

OtherASME PVP2006/ICPVT-11 Conference
CountryCanada
CityVancouver, BC
Period06/7/2306/7/27

Fingerprint

Application programming interfaces (API)
Pipe
Defects
Steel
Corrosion
Plastics

ASJC Scopus subject areas

  • Mechanical Engineering

Cite this

Oh, C. K., Kim, Y. J., Baek, J. H., Kim, Y. P., & Kim, W. S. (2006). Ductile failure analyses for API X65 pipes based on local failure criteria. In Proceedings of 2006 ASME Pressure Vessels and Piping Division Conference - ASME PVP2006/ICPVT-11 Conference - Pressure Vessel Technologies for the Global Community (American Society of Mechanical Engineers, Pressure Vessels and Piping Division (Publication) PVP; Vol. 2006). https://doi.org/10.1115/PVP2006-ICPVT-11-93769

Ductile failure analyses for API X65 pipes based on local failure criteria. / Oh, Chang Kyun; Kim, Yun Jae; Baek, Jong Hyun; Kim, Young Pyo; Kim, Woo Sik.

Proceedings of 2006 ASME Pressure Vessels and Piping Division Conference - ASME PVP2006/ICPVT-11 Conference - Pressure Vessel Technologies for the Global Community. 2006. (American Society of Mechanical Engineers, Pressure Vessels and Piping Division (Publication) PVP; Vol. 2006).

Research output: Chapter in Book/Report/Conference proceedingConference contribution

Oh, CK, Kim, YJ, Baek, JH, Kim, YP & Kim, WS 2006, Ductile failure analyses for API X65 pipes based on local failure criteria. in Proceedings of 2006 ASME Pressure Vessels and Piping Division Conference - ASME PVP2006/ICPVT-11 Conference - Pressure Vessel Technologies for the Global Community. American Society of Mechanical Engineers, Pressure Vessels and Piping Division (Publication) PVP, vol. 2006, ASME PVP2006/ICPVT-11 Conference, Vancouver, BC, Canada, 06/7/23. https://doi.org/10.1115/PVP2006-ICPVT-11-93769
Oh CK, Kim YJ, Baek JH, Kim YP, Kim WS. Ductile failure analyses for API X65 pipes based on local failure criteria. In Proceedings of 2006 ASME Pressure Vessels and Piping Division Conference - ASME PVP2006/ICPVT-11 Conference - Pressure Vessel Technologies for the Global Community. 2006. (American Society of Mechanical Engineers, Pressure Vessels and Piping Division (Publication) PVP). https://doi.org/10.1115/PVP2006-ICPVT-11-93769
Oh, Chang Kyun ; Kim, Yun Jae ; Baek, Jong Hyun ; Kim, Young Pyo ; Kim, Woo Sik. / Ductile failure analyses for API X65 pipes based on local failure criteria. Proceedings of 2006 ASME Pressure Vessels and Piping Division Conference - ASME PVP2006/ICPVT-11 Conference - Pressure Vessel Technologies for the Global Community. 2006. (American Society of Mechanical Engineers, Pressure Vessels and Piping Division (Publication) PVP).
@inproceedings{d2c78e5460694bfcbdc9b05ea121f082,
title = "Ductile failure analyses for API X65 pipes based on local failure criteria",
abstract = "A local failure criterion for the API X65 steel is applied to predict ductile failure of full-scale API X65 pipes with simulated corrosion and gouge defects under internal pressure. The local failure criterion is the stress-modified fracture strain for the API X65 steel as a function of the stress triaxiality (defined by the ratio of the hydrostatic stress to the effective stress). Based on detailed FE analyses with the proposed local failure criteria, burst pressures of defective pipes are estimated and compared with experimental data. The Failure of corroded pipes is governed by local necking and plastic collapse in the defective region, rather than failure. For pipes with gouge defects, on the other hand, it is found that fracture is dominant. The predicted burst pressures are in good agreement with experimental data. Noting that an assessment equation against the gouge defect is not yet available, parametric study is performed, from which a simple equation is proposed to predict burst pressure for API X65 pipes with gouge defects.",
author = "Oh, {Chang Kyun} and Kim, {Yun Jae} and Baek, {Jong Hyun} and Kim, {Young Pyo} and Kim, {Woo Sik}",
year = "2006",
month = "11",
day = "29",
doi = "10.1115/PVP2006-ICPVT-11-93769",
language = "English",
isbn = "0791837823",
series = "American Society of Mechanical Engineers, Pressure Vessels and Piping Division (Publication) PVP",
booktitle = "Proceedings of 2006 ASME Pressure Vessels and Piping Division Conference - ASME PVP2006/ICPVT-11 Conference - Pressure Vessel Technologies for the Global Community",

}

TY - GEN

T1 - Ductile failure analyses for API X65 pipes based on local failure criteria

AU - Oh, Chang Kyun

AU - Kim, Yun Jae

AU - Baek, Jong Hyun

AU - Kim, Young Pyo

AU - Kim, Woo Sik

PY - 2006/11/29

Y1 - 2006/11/29

N2 - A local failure criterion for the API X65 steel is applied to predict ductile failure of full-scale API X65 pipes with simulated corrosion and gouge defects under internal pressure. The local failure criterion is the stress-modified fracture strain for the API X65 steel as a function of the stress triaxiality (defined by the ratio of the hydrostatic stress to the effective stress). Based on detailed FE analyses with the proposed local failure criteria, burst pressures of defective pipes are estimated and compared with experimental data. The Failure of corroded pipes is governed by local necking and plastic collapse in the defective region, rather than failure. For pipes with gouge defects, on the other hand, it is found that fracture is dominant. The predicted burst pressures are in good agreement with experimental data. Noting that an assessment equation against the gouge defect is not yet available, parametric study is performed, from which a simple equation is proposed to predict burst pressure for API X65 pipes with gouge defects.

AB - A local failure criterion for the API X65 steel is applied to predict ductile failure of full-scale API X65 pipes with simulated corrosion and gouge defects under internal pressure. The local failure criterion is the stress-modified fracture strain for the API X65 steel as a function of the stress triaxiality (defined by the ratio of the hydrostatic stress to the effective stress). Based on detailed FE analyses with the proposed local failure criteria, burst pressures of defective pipes are estimated and compared with experimental data. The Failure of corroded pipes is governed by local necking and plastic collapse in the defective region, rather than failure. For pipes with gouge defects, on the other hand, it is found that fracture is dominant. The predicted burst pressures are in good agreement with experimental data. Noting that an assessment equation against the gouge defect is not yet available, parametric study is performed, from which a simple equation is proposed to predict burst pressure for API X65 pipes with gouge defects.

UR - http://www.scopus.com/inward/record.url?scp=33751342968&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=33751342968&partnerID=8YFLogxK

U2 - 10.1115/PVP2006-ICPVT-11-93769

DO - 10.1115/PVP2006-ICPVT-11-93769

M3 - Conference contribution

AN - SCOPUS:33751342968

SN - 0791837823

SN - 9780791837825

T3 - American Society of Mechanical Engineers, Pressure Vessels and Piping Division (Publication) PVP

BT - Proceedings of 2006 ASME Pressure Vessels and Piping Division Conference - ASME PVP2006/ICPVT-11 Conference - Pressure Vessel Technologies for the Global Community

ER -