Glycothermal synthesis of ZnGa2O4:Mn2+ nanophosphor and change in its photoluminescence intensity by heat-treatment

Masahiro Takesada, Tetsuhiko Isobe, Hisamitsu Takahashi, Shigeo Itoh

Research output: Contribution to journalArticle

12 Citations (Scopus)

Abstract

Zn Ga2 O4: Mn2+ nanophosphors were synthesized from zinc acetate dihydrate, gallium acetylacetonate, and manganese(II) acetate tetrahydrate in 1,4-butanediol by glycothermal method at 300°C for 2 h. Their average particle diameter was 12.1±2.5 nm. We investigated the influence of temperatures of postheat-treatment in Ar on the luminescent and structural properties. The photoluminescence (PL) intensity slightly decreased after heating below 900°C. The PL intensity increased between 900 and 1200°C, reached at the maximum at 1200°C and decreased over 1200°C. The decrease of the PL intensity by heating below 900°C occurred by the removal of adsorbed organic species. The X-ray diffraction profile indicated the decomposition of Zn Ga2 O4 to Ga2 O3 and ZnO by heating over 1200°C, resulting in the decrease of the PL intensity. The change in the integrated intensity of electron paramagnetic resonance due to paramagnetic Mn2+ with the temperature of heat-treatment in Ar was similar to that of the PL intensity. This suggests that the PL intensity is correlated to the incorporated Mn2+ amount.

Original languageEnglish
Pages (from-to)J136-J140
JournalJournal of the Electrochemical Society
Volume154
Issue number4
DOIs
Publication statusPublished - 2007 Mar 16

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Renewable Energy, Sustainability and the Environment
  • Surfaces, Coatings and Films
  • Electrochemistry
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Glycothermal synthesis of ZnGa<sub>2</sub>O<sub>4</sub>:Mn<sup>2+</sup> nanophosphor and change in its photoluminescence intensity by heat-treatment'. Together they form a unique fingerprint.

  • Cite this