Grain size effect on thermoelectric properties of PbTe prepared by spark plasma sintering

S. Yoneda, E. Ohta, H. T. Kaibe, I. J. Ohsugi, I. Shiota, I. A. Nishida

Research output: Contribution to journalArticle

17 Citations (Scopus)

Abstract

Sintered PbTe materials with average grain sizes of 28-309 μm were prepared by the spark plasma sintering technique. The apparent densities of the sintered PbTe were 8.17-8.23 Mg/m3, which were higher than 99% of the theoretical one. Thermoelectric properties of the sintered materials and those of the as-grown boule by Bridgman method were measured in the temperature range from 77 to 350 K. Resistivity, ρ of the sintered materials increased with decreasing grain size. Temperature dependence of ρ of the sintered PbTe was remarkably different from that of the as-grown boule below 250 K because of potential barriers at grain boundaries. Hall coefficient, RH of the sintered materials at room temperature increased from 1.4 x 10-6 to 3.4 x 10-6 m3/C, as the average grain size increased from 28 to 309 pm, which suggested that oxidation in the crystal grains was caused in the sintering process. Temperature dependence of the thermoelectric power, α of the sintered PbTe below 250 K reflected the effect of carrier scattering at grain boundaries. Lattice thermal conductivity of the sintered PbTe decreased with decreasing grain size below 250 K, while it was independent of the grain size above that temperature. Above 250 K, thermoelectric properties of the sintered PbTe, except those in the 28 μm grain case, were consistent with those of the as-grown boule. The values of α and RH at 295 K were calculated by using a two-valence-band model involving a non-parabolic and a parabolic valence band. The calculation results were in good agreement with the experimental data.

Original languageEnglish
Pages (from-to)329-335
Number of pages7
JournalMaterials Transactions
Volume42
Issue number2
Publication statusPublished - 2001

Fingerprint

Spark plasma sintering
sparks
sintering
grain size
Valence bands
Grain boundaries
Temperature
grain boundaries
valence
temperature dependence
Crystal growth from melt
Bridgman method
Thermoelectric power
Crystal lattices
Hall effect
Thermal conductivity
thermal conductivity
Sintering
Scattering
Oxidation

Keywords

  • Lead telluride
  • Non-parabolic valence band
  • Parabolic valence band
  • Potential barrier
  • Spark plasma sintering
  • Thermal conductivity
  • Thermoelectric property
  • Two-valence-band model

ASJC Scopus subject areas

  • Materials Science(all)
  • Metals and Alloys

Cite this

Yoneda, S., Ohta, E., Kaibe, H. T., Ohsugi, I. J., Shiota, I., & Nishida, I. A. (2001). Grain size effect on thermoelectric properties of PbTe prepared by spark plasma sintering. Materials Transactions, 42(2), 329-335.

Grain size effect on thermoelectric properties of PbTe prepared by spark plasma sintering. / Yoneda, S.; Ohta, E.; Kaibe, H. T.; Ohsugi, I. J.; Shiota, I.; Nishida, I. A.

In: Materials Transactions, Vol. 42, No. 2, 2001, p. 329-335.

Research output: Contribution to journalArticle

Yoneda, S, Ohta, E, Kaibe, HT, Ohsugi, IJ, Shiota, I & Nishida, IA 2001, 'Grain size effect on thermoelectric properties of PbTe prepared by spark plasma sintering', Materials Transactions, vol. 42, no. 2, pp. 329-335.
Yoneda S, Ohta E, Kaibe HT, Ohsugi IJ, Shiota I, Nishida IA. Grain size effect on thermoelectric properties of PbTe prepared by spark plasma sintering. Materials Transactions. 2001;42(2):329-335.
Yoneda, S. ; Ohta, E. ; Kaibe, H. T. ; Ohsugi, I. J. ; Shiota, I. ; Nishida, I. A. / Grain size effect on thermoelectric properties of PbTe prepared by spark plasma sintering. In: Materials Transactions. 2001 ; Vol. 42, No. 2. pp. 329-335.
@article{0232ef794ad2429c91aa980c426c455e,
title = "Grain size effect on thermoelectric properties of PbTe prepared by spark plasma sintering",
abstract = "Sintered PbTe materials with average grain sizes of 28-309 μm were prepared by the spark plasma sintering technique. The apparent densities of the sintered PbTe were 8.17-8.23 Mg/m3, which were higher than 99{\%} of the theoretical one. Thermoelectric properties of the sintered materials and those of the as-grown boule by Bridgman method were measured in the temperature range from 77 to 350 K. Resistivity, ρ of the sintered materials increased with decreasing grain size. Temperature dependence of ρ of the sintered PbTe was remarkably different from that of the as-grown boule below 250 K because of potential barriers at grain boundaries. Hall coefficient, RH of the sintered materials at room temperature increased from 1.4 x 10-6 to 3.4 x 10-6 m3/C, as the average grain size increased from 28 to 309 pm, which suggested that oxidation in the crystal grains was caused in the sintering process. Temperature dependence of the thermoelectric power, α of the sintered PbTe below 250 K reflected the effect of carrier scattering at grain boundaries. Lattice thermal conductivity of the sintered PbTe decreased with decreasing grain size below 250 K, while it was independent of the grain size above that temperature. Above 250 K, thermoelectric properties of the sintered PbTe, except those in the 28 μm grain case, were consistent with those of the as-grown boule. The values of α and RH at 295 K were calculated by using a two-valence-band model involving a non-parabolic and a parabolic valence band. The calculation results were in good agreement with the experimental data.",
keywords = "Lead telluride, Non-parabolic valence band, Parabolic valence band, Potential barrier, Spark plasma sintering, Thermal conductivity, Thermoelectric property, Two-valence-band model",
author = "S. Yoneda and E. Ohta and Kaibe, {H. T.} and Ohsugi, {I. J.} and I. Shiota and Nishida, {I. A.}",
year = "2001",
language = "English",
volume = "42",
pages = "329--335",
journal = "Materials Transactions",
issn = "1345-9678",
publisher = "Japan Institute of Metals (JIM)",
number = "2",

}

TY - JOUR

T1 - Grain size effect on thermoelectric properties of PbTe prepared by spark plasma sintering

AU - Yoneda, S.

AU - Ohta, E.

AU - Kaibe, H. T.

AU - Ohsugi, I. J.

AU - Shiota, I.

AU - Nishida, I. A.

PY - 2001

Y1 - 2001

N2 - Sintered PbTe materials with average grain sizes of 28-309 μm were prepared by the spark plasma sintering technique. The apparent densities of the sintered PbTe were 8.17-8.23 Mg/m3, which were higher than 99% of the theoretical one. Thermoelectric properties of the sintered materials and those of the as-grown boule by Bridgman method were measured in the temperature range from 77 to 350 K. Resistivity, ρ of the sintered materials increased with decreasing grain size. Temperature dependence of ρ of the sintered PbTe was remarkably different from that of the as-grown boule below 250 K because of potential barriers at grain boundaries. Hall coefficient, RH of the sintered materials at room temperature increased from 1.4 x 10-6 to 3.4 x 10-6 m3/C, as the average grain size increased from 28 to 309 pm, which suggested that oxidation in the crystal grains was caused in the sintering process. Temperature dependence of the thermoelectric power, α of the sintered PbTe below 250 K reflected the effect of carrier scattering at grain boundaries. Lattice thermal conductivity of the sintered PbTe decreased with decreasing grain size below 250 K, while it was independent of the grain size above that temperature. Above 250 K, thermoelectric properties of the sintered PbTe, except those in the 28 μm grain case, were consistent with those of the as-grown boule. The values of α and RH at 295 K were calculated by using a two-valence-band model involving a non-parabolic and a parabolic valence band. The calculation results were in good agreement with the experimental data.

AB - Sintered PbTe materials with average grain sizes of 28-309 μm were prepared by the spark plasma sintering technique. The apparent densities of the sintered PbTe were 8.17-8.23 Mg/m3, which were higher than 99% of the theoretical one. Thermoelectric properties of the sintered materials and those of the as-grown boule by Bridgman method were measured in the temperature range from 77 to 350 K. Resistivity, ρ of the sintered materials increased with decreasing grain size. Temperature dependence of ρ of the sintered PbTe was remarkably different from that of the as-grown boule below 250 K because of potential barriers at grain boundaries. Hall coefficient, RH of the sintered materials at room temperature increased from 1.4 x 10-6 to 3.4 x 10-6 m3/C, as the average grain size increased from 28 to 309 pm, which suggested that oxidation in the crystal grains was caused in the sintering process. Temperature dependence of the thermoelectric power, α of the sintered PbTe below 250 K reflected the effect of carrier scattering at grain boundaries. Lattice thermal conductivity of the sintered PbTe decreased with decreasing grain size below 250 K, while it was independent of the grain size above that temperature. Above 250 K, thermoelectric properties of the sintered PbTe, except those in the 28 μm grain case, were consistent with those of the as-grown boule. The values of α and RH at 295 K were calculated by using a two-valence-band model involving a non-parabolic and a parabolic valence band. The calculation results were in good agreement with the experimental data.

KW - Lead telluride

KW - Non-parabolic valence band

KW - Parabolic valence band

KW - Potential barrier

KW - Spark plasma sintering

KW - Thermal conductivity

KW - Thermoelectric property

KW - Two-valence-band model

UR - http://www.scopus.com/inward/record.url?scp=0035009620&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0035009620&partnerID=8YFLogxK

M3 - Article

AN - SCOPUS:0035009620

VL - 42

SP - 329

EP - 335

JO - Materials Transactions

JF - Materials Transactions

SN - 1345-9678

IS - 2

ER -