Redox-induced dual optical switching of CaTiO3:Pr3+ phosphor nanoparticles synthesized by sol–gel method

Hideaki Takahashi, Manabu Hagiwara, Shinobu Fujihara

Research output: Contribution to journalArticlepeer-review

Abstract

Red-emitting CaTiO3:Pr3+ phosphor nanoparticles were synthesized by a sol–gel method with a final heat treatment at a low temperature of 650 °C. For comparison, the CaTiO3:Pr3+ phosphor was also synthesized by a conventional solid-state reaction method conducted at 1250 °C. The two kinds of resultant CaTiO3:Pr3+ samples were revealed to differ largely in their microstructure and optical properties. Diffuse reflectance and photoluminescence measurements suggested that the sample from the solid-state reaction possessed a larger number of defects, which would deteriorate the optical properties, due to heating at high temperature. On the other hand, the sol–gel-derived sample exhibited much better optical properties and thus it was used for evaluating optical-switching phenomena upon redox treatments. In photoluminescence, three excitation bands were observed at 265, 335, and 375 nm for the red emission of the CaTiO3:Pr3+ sample, and one of them (375 nm) was more effective for inducing luminescence quenching by a reduction treatment at room temperature. A body color of the CaTiO3:Pr3+ sample was also changed from white to light yellow by the reduction due to the enhanced visible-light absorption. Such the dual luminescence/absorption switching was shown to be reversible with a subsequent oxidation and repeatable with a consecutive redox treatment. [Figure not available: see fulltext.]

Original languageEnglish
JournalJournal of Sol-Gel Science and Technology
DOIs
Publication statusAccepted/In press - 2022

Keywords

  • CaTiO:Pr
  • Nanoparticles
  • Optical switching
  • Phosphors
  • Photoluminescence
  • Redox reaction

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Ceramics and Composites
  • Chemistry(all)
  • Biomaterials
  • Condensed Matter Physics
  • Materials Chemistry

Fingerprint

Dive into the research topics of 'Redox-induced dual optical switching of CaTiO3:Pr3+ phosphor nanoparticles synthesized by sol–gel method'. Together they form a unique fingerprint.

Cite this