Relationship between optical properties and crystallinity of nanometer Y2O3: Eu phosphor

T. Igarashi, M. Ihara, T. Kusunoki, K. Ohno, T. Isobe, M. Senna

Research output: Contribution to journalArticlepeer-review

248 Citations (Scopus)

Abstract

Y2O3-doped Eu3+ (Y2O3:Eu) nanometer particles (NPs) were synthesized via a chemical route. The particle size estimated by x-ray diffractometry and transmission electron microscopy was about 61 nm. Two photoluminescence peaks were observed at 582 and 587 nm, being attributed to the transition of 5D07F1a of Eu3+ in the S6 and C2 symmetry sites of Y2O3, respectively. The intensity ratio of the photoluminescence peaks at 582 nm to at 587 nm was larger for NPs than for micrometer particles (MPs). The excitation peak of NPs due to the charge-transfer band shifted toward the high-energy side as compared with that of MPs. According to x-ray diffractometry, the lattice distortion and the lattice constant were larger for NPs than for MPs, showing the restructure at the near surface and the increase in ionicity of the Eu-O bond with decreasing particle size. This explains the blueshift in the excitation peak.

Original languageEnglish
Pages (from-to)1549-1551
Number of pages3
JournalApplied Physics Letters
Volume76
Issue number12
DOIs
Publication statusPublished - 2000 Mar 20

ASJC Scopus subject areas

  • Physics and Astronomy (miscellaneous)

Fingerprint Dive into the research topics of 'Relationship between optical properties and crystallinity of nanometer Y<sub>2</sub>O<sub>3</sub>: Eu phosphor'. Together they form a unique fingerprint.

Cite this