Stable iridium-modified boron-doped diamond electrode for the application in electrochemical detection of arsenic (III)

Tia Agustiany, Munawar Khalil, Yasuaki Einaga, Prastika K. Jiwanti, Tribidasari A. Ivandini

Research output: Contribution to journalArticle


Preparation of stable iridium-modified boron-doped diamond electrodes through electrodeposition was studied. The electrode was prepared by wet chemical seeding and thermal annealing that performed before and after the electrodeposition process in order to get a homogeneous deposition. The modified electrode from each step was characterized using scanning electron microscopy-energy dispersive spectroscopy (SEM-EDS), Raman and X-Ray photoelectron spectroscopy (XPS) to understand the surface topography and its elemental composition. In addition, cyclic voltammetry for arsenic (III) was performed to examine the electrochemical behavior of the modified diamond. At an optimum condition in a phosphate buffer solution pH 3 and a scan rate of 50 mV/s, a linear calibration curve in the concentration range of 1–100 μM with a detection limit of 4.64 μM was achieved. Excellent stability and repeatability were also observed with relative standard deviations of 2.6% and <0.4%, respectively. Additionally, the electrode exhibited good linearity and sensitivity towards the measurement of arsenic (III) in both arsenic (III)-added tap water and lake water samples.

Original languageEnglish
Article number122723
JournalMaterials Chemistry and Physics
Publication statusPublished - 2020 Apr 1



  • Arsenic detection
  • Boron-doped diamond
  • Homogeneous electrodeposition
  • Iridium-modification
  • Wet-chemical seeding

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics

Cite this