Synthesis of L10-(FeyPt100-y) 100-xCux nanoparticles with high coercivity by annealing at 400 °C

Hiroaki Kura, Tetsuya Sato

Research output: Contribution to journalArticle

10 Citations (Scopus)

Abstract

(FeyPt100-y)100-xCux nanoparticles with various compositions were synthesized by the simultaneous polyol reduction of Pt(acac)2 and Cu(acac)2 and the thermal decomposition of Fe(CO)5. The as-made particles had a disordered fee structure and an average diameter of ∼4.8 nm. The result of x-ray diffraction indicated a transformation from fee structure to fct structure in some samples after annealing at 400 °C for 1 h, and the c/a ratio of lattice constant decreased with increasing Cu content. The doping of Cu clearly plays a significant role on the reduction of the ordering temperature in the ternary (FeyPt100-y)100-xCUx alloy. In addition, the ordering of (FeyPt100-y) 100-xCux nanoparticles is significantly dependent on the composition of Fe and Pt. As a result, (Fe47Pt53) 74Cu26 nanoparticles have the coercive fields of ∼10 and ∼2 kOe at 10 K and room temperature, respectively.

Original languageEnglish
Pages (from-to)5771-5774
Number of pages4
JournalJournal of Applied Physics
Volume96
Issue number10
DOIs
Publication statusPublished - 2004 Nov 15

Fingerprint

coercivity
nanoparticles
annealing
synthesis
thermal decomposition
x ray diffraction
temperature
room temperature

ASJC Scopus subject areas

  • Physics and Astronomy (miscellaneous)
  • Physics and Astronomy(all)

Cite this

Synthesis of L10-(FeyPt100-y) 100-xCux nanoparticles with high coercivity by annealing at 400 °C. / Kura, Hiroaki; Sato, Tetsuya.

In: Journal of Applied Physics, Vol. 96, No. 10, 15.11.2004, p. 5771-5774.

Research output: Contribution to journalArticle

@article{fbb36e5062914eb98554e3e410628022,
title = "Synthesis of L10-(FeyPt100-y) 100-xCux nanoparticles with high coercivity by annealing at 400 °C",
abstract = "(FeyPt100-y)100-xCux nanoparticles with various compositions were synthesized by the simultaneous polyol reduction of Pt(acac)2 and Cu(acac)2 and the thermal decomposition of Fe(CO)5. The as-made particles had a disordered fee structure and an average diameter of ∼4.8 nm. The result of x-ray diffraction indicated a transformation from fee structure to fct structure in some samples after annealing at 400 °C for 1 h, and the c/a ratio of lattice constant decreased with increasing Cu content. The doping of Cu clearly plays a significant role on the reduction of the ordering temperature in the ternary (FeyPt100-y)100-xCUx alloy. In addition, the ordering of (FeyPt100-y) 100-xCux nanoparticles is significantly dependent on the composition of Fe and Pt. As a result, (Fe47Pt53) 74Cu26 nanoparticles have the coercive fields of ∼10 and ∼2 kOe at 10 K and room temperature, respectively.",
author = "Hiroaki Kura and Tetsuya Sato",
year = "2004",
month = "11",
day = "15",
doi = "10.1063/1.1803919",
language = "English",
volume = "96",
pages = "5771--5774",
journal = "Journal of Applied Physics",
issn = "0021-8979",
publisher = "American Institute of Physics Publising LLC",
number = "10",

}

TY - JOUR

T1 - Synthesis of L10-(FeyPt100-y) 100-xCux nanoparticles with high coercivity by annealing at 400 °C

AU - Kura, Hiroaki

AU - Sato, Tetsuya

PY - 2004/11/15

Y1 - 2004/11/15

N2 - (FeyPt100-y)100-xCux nanoparticles with various compositions were synthesized by the simultaneous polyol reduction of Pt(acac)2 and Cu(acac)2 and the thermal decomposition of Fe(CO)5. The as-made particles had a disordered fee structure and an average diameter of ∼4.8 nm. The result of x-ray diffraction indicated a transformation from fee structure to fct structure in some samples after annealing at 400 °C for 1 h, and the c/a ratio of lattice constant decreased with increasing Cu content. The doping of Cu clearly plays a significant role on the reduction of the ordering temperature in the ternary (FeyPt100-y)100-xCUx alloy. In addition, the ordering of (FeyPt100-y) 100-xCux nanoparticles is significantly dependent on the composition of Fe and Pt. As a result, (Fe47Pt53) 74Cu26 nanoparticles have the coercive fields of ∼10 and ∼2 kOe at 10 K and room temperature, respectively.

AB - (FeyPt100-y)100-xCux nanoparticles with various compositions were synthesized by the simultaneous polyol reduction of Pt(acac)2 and Cu(acac)2 and the thermal decomposition of Fe(CO)5. The as-made particles had a disordered fee structure and an average diameter of ∼4.8 nm. The result of x-ray diffraction indicated a transformation from fee structure to fct structure in some samples after annealing at 400 °C for 1 h, and the c/a ratio of lattice constant decreased with increasing Cu content. The doping of Cu clearly plays a significant role on the reduction of the ordering temperature in the ternary (FeyPt100-y)100-xCUx alloy. In addition, the ordering of (FeyPt100-y) 100-xCux nanoparticles is significantly dependent on the composition of Fe and Pt. As a result, (Fe47Pt53) 74Cu26 nanoparticles have the coercive fields of ∼10 and ∼2 kOe at 10 K and room temperature, respectively.

UR - http://www.scopus.com/inward/record.url?scp=9944261463&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=9944261463&partnerID=8YFLogxK

U2 - 10.1063/1.1803919

DO - 10.1063/1.1803919

M3 - Article

AN - SCOPUS:9944261463

VL - 96

SP - 5771

EP - 5774

JO - Journal of Applied Physics

JF - Journal of Applied Physics

SN - 0021-8979

IS - 10

ER -