Tensile and high cycle fatigue tests of NiCo thin films

Jun Hyub Park, Yun Bae Chun, Yun Jae Kim, Yong Hak Huh, Dong Joong Kang

Research output: Contribution to journalArticle

1 Citation (Scopus)

Abstract

This paper represents the results of tensile and fatigue tests of NiCo thin films, to investigate the effect of size on mechanical properties. The "dog-bone" type Specimen with reduced section widths of 50 μm and 150 μm were fabricated on two 6 inch wafers using electro-plating process and MEMS processes. The NiCo film thickness of one wafer was 7.23 μm. The elastic moduli of the NiCo thin film specimens were about 183±4.1 GPa for the 50 μm specimens and about 148±8.4 GPa for 150 μm specimens. The ultimate tensile strengths for the 50 μm and 150 μm width specimens were 2431±87.8 and 2348±93.3 MPa, respectively. However, the difference between the tensile strengths of the specimens is low, at 3.3%. Fatigue tests were performed with 2 or 5 Hz in atmospheric air at room temperature under axial loading at a load ratio of R (=Fmin/F max) = 0.1 in a load-control until complete failure. Fatigue strength coefficients of the specimens with 50 and 150 μm width were 1785 and 1257 MPa, respectively. In addition, fatigue strength exponents of the specimens with 50 and 150 μm width were -0.0818 and -0.0629, respectively.

Original languageEnglish
Pages (from-to)1303-1308
Number of pages6
JournalProcedia Engineering
Volume10
DOIs
Publication statusPublished - 2011 Jan 1
Externally publishedYes

Fingerprint

Tensile strength
Fatigue of materials
Thin films
Plating
MEMS
Film thickness
Bone
Elastic moduli
Mechanical properties
Air
Temperature
Fatigue strength

Keywords

  • Fatigue high test
  • Fatigue properties
  • NiCo thin film
  • Tensile properties
  • Tensile test

ASJC Scopus subject areas

  • Engineering(all)

Cite this

Tensile and high cycle fatigue tests of NiCo thin films. / Park, Jun Hyub; Chun, Yun Bae; Kim, Yun Jae; Huh, Yong Hak; Kang, Dong Joong.

In: Procedia Engineering, Vol. 10, 01.01.2011, p. 1303-1308.

Research output: Contribution to journalArticle

Park, Jun Hyub ; Chun, Yun Bae ; Kim, Yun Jae ; Huh, Yong Hak ; Kang, Dong Joong. / Tensile and high cycle fatigue tests of NiCo thin films. In: Procedia Engineering. 2011 ; Vol. 10. pp. 1303-1308.
@article{22e3a49db7c742ceae91db4878709c2f,
title = "Tensile and high cycle fatigue tests of NiCo thin films",
abstract = "This paper represents the results of tensile and fatigue tests of NiCo thin films, to investigate the effect of size on mechanical properties. The {"}dog-bone{"} type Specimen with reduced section widths of 50 μm and 150 μm were fabricated on two 6 inch wafers using electro-plating process and MEMS processes. The NiCo film thickness of one wafer was 7.23 μm. The elastic moduli of the NiCo thin film specimens were about 183±4.1 GPa for the 50 μm specimens and about 148±8.4 GPa for 150 μm specimens. The ultimate tensile strengths for the 50 μm and 150 μm width specimens were 2431±87.8 and 2348±93.3 MPa, respectively. However, the difference between the tensile strengths of the specimens is low, at 3.3{\%}. Fatigue tests were performed with 2 or 5 Hz in atmospheric air at room temperature under axial loading at a load ratio of R (=Fmin/F max) = 0.1 in a load-control until complete failure. Fatigue strength coefficients of the specimens with 50 and 150 μm width were 1785 and 1257 MPa, respectively. In addition, fatigue strength exponents of the specimens with 50 and 150 μm width were -0.0818 and -0.0629, respectively.",
keywords = "Fatigue high test, Fatigue properties, NiCo thin film, Tensile properties, Tensile test",
author = "Park, {Jun Hyub} and Chun, {Yun Bae} and Kim, {Yun Jae} and Huh, {Yong Hak} and Kang, {Dong Joong}",
year = "2011",
month = "1",
day = "1",
doi = "10.1016/j.proeng.2011.04.217",
language = "English",
volume = "10",
pages = "1303--1308",
journal = "Procedia Engineering",
issn = "1877-7058",
publisher = "Elsevier BV",

}

TY - JOUR

T1 - Tensile and high cycle fatigue tests of NiCo thin films

AU - Park, Jun Hyub

AU - Chun, Yun Bae

AU - Kim, Yun Jae

AU - Huh, Yong Hak

AU - Kang, Dong Joong

PY - 2011/1/1

Y1 - 2011/1/1

N2 - This paper represents the results of tensile and fatigue tests of NiCo thin films, to investigate the effect of size on mechanical properties. The "dog-bone" type Specimen with reduced section widths of 50 μm and 150 μm were fabricated on two 6 inch wafers using electro-plating process and MEMS processes. The NiCo film thickness of one wafer was 7.23 μm. The elastic moduli of the NiCo thin film specimens were about 183±4.1 GPa for the 50 μm specimens and about 148±8.4 GPa for 150 μm specimens. The ultimate tensile strengths for the 50 μm and 150 μm width specimens were 2431±87.8 and 2348±93.3 MPa, respectively. However, the difference between the tensile strengths of the specimens is low, at 3.3%. Fatigue tests were performed with 2 or 5 Hz in atmospheric air at room temperature under axial loading at a load ratio of R (=Fmin/F max) = 0.1 in a load-control until complete failure. Fatigue strength coefficients of the specimens with 50 and 150 μm width were 1785 and 1257 MPa, respectively. In addition, fatigue strength exponents of the specimens with 50 and 150 μm width were -0.0818 and -0.0629, respectively.

AB - This paper represents the results of tensile and fatigue tests of NiCo thin films, to investigate the effect of size on mechanical properties. The "dog-bone" type Specimen with reduced section widths of 50 μm and 150 μm were fabricated on two 6 inch wafers using electro-plating process and MEMS processes. The NiCo film thickness of one wafer was 7.23 μm. The elastic moduli of the NiCo thin film specimens were about 183±4.1 GPa for the 50 μm specimens and about 148±8.4 GPa for 150 μm specimens. The ultimate tensile strengths for the 50 μm and 150 μm width specimens were 2431±87.8 and 2348±93.3 MPa, respectively. However, the difference between the tensile strengths of the specimens is low, at 3.3%. Fatigue tests were performed with 2 or 5 Hz in atmospheric air at room temperature under axial loading at a load ratio of R (=Fmin/F max) = 0.1 in a load-control until complete failure. Fatigue strength coefficients of the specimens with 50 and 150 μm width were 1785 and 1257 MPa, respectively. In addition, fatigue strength exponents of the specimens with 50 and 150 μm width were -0.0818 and -0.0629, respectively.

KW - Fatigue high test

KW - Fatigue properties

KW - NiCo thin film

KW - Tensile properties

KW - Tensile test

UR - http://www.scopus.com/inward/record.url?scp=80052937780&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=80052937780&partnerID=8YFLogxK

U2 - 10.1016/j.proeng.2011.04.217

DO - 10.1016/j.proeng.2011.04.217

M3 - Article

AN - SCOPUS:80052937780

VL - 10

SP - 1303

EP - 1308

JO - Procedia Engineering

JF - Procedia Engineering

SN - 1877-7058

ER -