A high glass transition temperature, thermally stable and transparent polymer for plastic optical fiber; a novel copolymer of methyl methacrylate with npentafluorophenyl maleimide

Yoshiyuki Okamoto, Liping Lou, Kotaro Koike, Yasuhiro Koike

研究成果: Paper査読

抄録

N-pentafluorophenyl maleimide (PFPMI) was synthesized. The homo and copolymers of PFPMI with methyl methacrylate (MMA) were prepared. The refractive indexes of poly(PFPMI) and PMMA are almost the same, 1.4989 and 1.4953 at 532 nm respectively. Therefore, the copolymers of PFPMI and MMA exhibited no light scattering and the film was very transparent. The glass transition temperatures of the PFPMI-co-MMA were in the range of 140°-180°and the refractive indexes were 1.4965-1.4970 with the PFPMI content from 18.8-65 mol%. In addition, the copolymers obtained have high thermal stability (~370°) and low water absorption property.

本文言語English
ページ139-142
ページ数4
出版ステータスPublished - 2011 12月 1
イベント20th International Conference on Plastic Optical Fibers, POF 2011 - Bilbao, Spain
継続期間: 2011 9月 142011 9月 16

Other

Other20th International Conference on Plastic Optical Fibers, POF 2011
国/地域Spain
CityBilbao
Period11/9/1411/9/16

ASJC Scopus subject areas

  • 電子材料、光学材料、および磁性材料
  • 材料化学
  • ポリマーおよびプラスチック

フィンガープリント

「A high glass transition temperature, thermally stable and transparent polymer for plastic optical fiber; a novel copolymer of methyl methacrylate with npentafluorophenyl maleimide」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル