Anisotropy of synthetic diamond in catalytic etching using iron powder

Junsha Wang, Long Wan, Jing Chen, Jiwang Yan

研究成果: Article査読

26 被引用数 (Scopus)

抄録

This paper demonstrated a novel technique for catalytic etching of synthetic diamond crystallites using iron (Fe) powder without flowing gas. The effect of temperature on the etching behaviour on different crystal planes of diamond was investigated. The surface morphology and surface roughness of the processed diamond were examined by scanning electron microscope (SEM) and laser-probe surface profiling. In addition, the material composition of the Fe-treated diamond was characterized using micro-Raman spectroscopy and the distribution of chemical elements and structural changes on Fe-loaded diamond surfaces were analyzed by energy dispersive X-ray spectroscopy (EDS) and X-ray diffraction (XRD), respectively. Results showed that at the same temperature the {1 0 0} plane was etched faster than the {1 1 1} plane, and that the etching rate of both {1 0 0} and {1 1 1} plane increased with temperature. The etch pits on {1 0 0} plane were reversed pyramid with flat {1 1 1} walls, while the etch holes on {1 1 1} plane were characterized with flat bottom. It was also demonstrated that graphitization of diamond and subsequent carbon diffusion in molten iron were two main factors resulting in the removal of carbon from the diamond surface.

本文言語English
ページ(範囲)388-393
ページ数6
ジャーナルApplied Surface Science
346
DOI
出版ステータスPublished - 2015 8 15

ASJC Scopus subject areas

  • 化学 (全般)
  • 凝縮系物理学
  • 物理学および天文学(全般)
  • 表面および界面
  • 表面、皮膜および薄膜

フィンガープリント

「Anisotropy of synthetic diamond in catalytic etching using iron powder」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル