TY - JOUR
T1 - Comparison of MA processes and products from Ni(OH)2 with Al or Al(OH)3
AU - Sekino, S.
AU - Senna, M.
AU - Isobe, T.
AU - Shinohara, T.
AU - Wagatsuma, F.
PY - 2001/1/1
Y1 - 2001/1/1
N2 - Ni(OH)2 was milled either with Al metal or with Al(OH)3 particles to compare the process of compounding and the properties of the products. Although the Knight shift, 27K, of 27Al-NMR spectrum of Al(OH)3 is about 0ppm, it exceeds 10000ppm after milling with Ni(OH)2 for 12h. This shift increases to above 20000ppm at lower temperature. In metallic Al system, 27K under the same condition was ca. 1600ppm and slightly decreases with decreasing temperature. In the latter system, the average conduction electron density of metallic Al is reduced by Ni species in the surface oxide layer, and reduces the Fermi contact interaction at Al nuclei to change the Knight shift. In contrast, in Al(OH)3 system, Al(III) species are surrounded by Ni(II) so that 27K is directly influenced by the local magnetic field of Ni(II). From the viewpoint of materials synthesis, using Al(OH)3 is more beneficial due to much more homogeneous structure close to that of NiAl2O4. We further elucidated the change in the state of Al by heating the as-milled product to give well-crystallized NiAl2O4. 27Al-NMR, 27K-X Plot, Homogeneity, Mechanochemical Reaction, NiAl2O4.
AB - Ni(OH)2 was milled either with Al metal or with Al(OH)3 particles to compare the process of compounding and the properties of the products. Although the Knight shift, 27K, of 27Al-NMR spectrum of Al(OH)3 is about 0ppm, it exceeds 10000ppm after milling with Ni(OH)2 for 12h. This shift increases to above 20000ppm at lower temperature. In metallic Al system, 27K under the same condition was ca. 1600ppm and slightly decreases with decreasing temperature. In the latter system, the average conduction electron density of metallic Al is reduced by Ni species in the surface oxide layer, and reduces the Fermi contact interaction at Al nuclei to change the Knight shift. In contrast, in Al(OH)3 system, Al(III) species are surrounded by Ni(II) so that 27K is directly influenced by the local magnetic field of Ni(II). From the viewpoint of materials synthesis, using Al(OH)3 is more beneficial due to much more homogeneous structure close to that of NiAl2O4. We further elucidated the change in the state of Al by heating the as-milled product to give well-crystallized NiAl2O4. 27Al-NMR, 27K-X Plot, Homogeneity, Mechanochemical Reaction, NiAl2O4.
UR - http://www.scopus.com/inward/record.url?scp=0035020289&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=0035020289&partnerID=8YFLogxK
M3 - Conference article
AN - SCOPUS:0035020289
VL - 360-362
SP - 409
EP - 414
JO - Materials Science Forum
JF - Materials Science Forum
SN - 0255-5476
T2 - Metastable, Mechanically Alloyed and Nanocrystalline Materials (ISMANAM 2000)
Y2 - 9 July 2000 through 14 July 2000
ER -