Controlled radical polymerization of styrene with magnetic iron oxides prepared through hydrothermal, bioinspired, and bacterial processes

Arihiro Kanazawa, Kotaro Satoh, Shokyoku Kanaoka, Masato Kakihana, Makoto Kobayashi, Junki Sato, Hiroaki Imai, Yuya Oaki, Atsushi Arakaki, Kiyofumi Katagiri, Masami Kamigaito, Sadahito Aoshima

研究成果: Article査読

2 被引用数 (Scopus)

抄録

Controlled/living radical polymerization was examined with the use of magnetic iron oxide (Fe3O4) prepared through various processes, including hydrothermal synthesis, a bioinspired process, and magnetotactic bacteria. Prior to the use of various types of Fe3O4, commercially available Fe3O4 was employed as a heterogeneous catalyst for styrene polymerization in conjunction with an alkyl halide as an initiator. Under appropriately optimized conditions, with the addition of Ph3P in a solvent mixture of toluene and DMF, the polymerization proceeded in a well-controlled manner. In addition, solid Fe3O4 was recovered using a magnetic approach and was reused for a polymerization reaction. The effects of stirring on the polymerization rate suggest that the surface of Fe3O4 is responsible for the catalysis in polymerization. Fe3O4 samples prepared through various processes were then used for styrene polymerization and showed different activities depending on the preparation process. In particular, Fe3O4 prepared through hydrothermal synthesis exhibited a much higher activity compared with commercial Fe3O4.

本文言語English
ページ(範囲)51122-51129
ページ数8
ジャーナルRSC Advances
5
63
DOI
出版ステータスPublished - 2015

ASJC Scopus subject areas

  • 化学 (全般)
  • 化学工学(全般)

フィンガープリント

「Controlled radical polymerization of styrene with magnetic iron oxides prepared through hydrothermal, bioinspired, and bacterial processes」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル