Dense proton injection into phosphate glasses using corona discharge treatment

Takuya Kinoshita, Atsushi Miyazaki, Keiga Kawaguchi, Daisuke Sakai, Takuya Yamaguchi, Takahisa Omata, Tomohiro Ishiyama, Masaya Fujioka, Hideo Kaiju, Junji Nishii

研究成果: Article査読

2 被引用数 (Scopus)

抄録

Sodium ions in 25NaO 1/2 -6LaO 3/2 -6GeO 2 -63PO 5/2 (mol%) glasses were substituted with protons using corona discharge treatment (CDT) under a H 2 atmosphere. The substitution of sodium ion to proton proceeded from the anode side to the cathode side with constant current flow during the CDT. A crystalline free and transparent glass plate of 0.3 mm thickness was obtained after CDT for 96 h. The maximum decrease rate from sodium ion to proton was 78 ± 10%. The proton conductivity of 8.5 × 10 −4 S/cm was attained at 400 °C.

本文言語English
ページ(範囲)718-722
ページ数5
ジャーナルApplied Surface Science
428
DOI
出版ステータスPublished - 2018 1 15
外部発表はい

ASJC Scopus subject areas

  • 化学 (全般)
  • 凝縮系物理学
  • 物理学および天文学(全般)
  • 表面および界面
  • 表面、皮膜および薄膜

フィンガープリント

「Dense proton injection into phosphate glasses using corona discharge treatment」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル