Effect of hydrothermal treatment on sinterability of hydroxyapatite

D. Kawagoe, H. Fujimori, S. Goto, N. Yamasaki, K. Ioku

研究成果: Conference contribution

抄録

Calcium hydroxyapatite, Ca10(PO4)6(OH) 2:HA, is the inorganic principle component of natural bones and teeth. It has been already suggested that the amount of OH ion in the crystal structure of HA is closely related to the biocompatibility. The amount of OH ion in current HA, however, has not been controlled. In order to prepare more functional HA ceramics, the amount of OH ion must be controlled. In this study, HA ceramics with different OH amount were prepared from fine HA crystals by spark plasma sintering (SPS). Fine powder of HA was treated hydrothermally at 200 °C for 24 h with pH 10 NH3 aqueous solution. The samples were pressed uniaxialy under 60 MPa, and then they were SPS at 800 °C, 900 °C and 1000 °C for 10 min with the heating rate of 25 °Cmin -1. No phases other than HA were revealed by XRD for the starting samples after hydrothermal treatment and samples after sintering by SPS at 800 °C, 900 °C and 1000 °C for 10 min. The quantity of OH ion in HA ceramics sintered by SPS was decreased with increasing temperature of sintering. Transparent HA ceramics were prepared by SPS at 900 °C and 1000 °C.

本文言語English
ホスト出版物のタイトルWATER DYNAMICS
ホスト出版物のサブタイトル3rd International Workshop on Water Dynamics
ページ108-111
ページ数4
DOI
出版ステータスPublished - 2006 5月 15
外部発表はい
イベントWATER DYANMICS: 3rd International Workshop on Water Dynamics - Sendai, Japan
継続期間: 2005 11月 162005 11月 17

出版物シリーズ

名前AIP Conference Proceedings
833
ISSN(印刷版)0094-243X
ISSN(電子版)1551-7616

Other

OtherWATER DYANMICS: 3rd International Workshop on Water Dynamics
国/地域Japan
CitySendai
Period05/11/1605/11/17

ASJC Scopus subject areas

  • 物理学および天文学(全般)

フィンガープリント

「Effect of hydrothermal treatment on sinterability of hydroxyapatite」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル