Fatigue properties of steel with super rapid induction localized quenching

Kengo Fukazawa, Masaru Koizumi, Jun Komotori, Masao Shimizu, Yoshitaka Misaka, Kazuhiro Kawasaki

研究成果: Article査読

抄録

The aim of the present study is to make clear the factors controlling the fatigue strength of the locally hardened machine parts. Rotational bending fatigue tests were performed with special focus on the effect of a peak tensile residual stress generated at the quenching boundary on the fatigue properties of the super rapid induction hardened steel. Results are summarized as follows. (1) The final failure starts at the position of the specimen surface where the peak tensile residual stress has been generated near the quenching boundary. (2) The fatigue strength at 107 cycles of the locallyhardened specimen is inferior to that of the non-hardened one because of such a peak tensile residual stress. (3) The effect of the peak tensile residual stress on the fatigue strength becomes smaller at higher stress amplitude because the relaxation of the residual stress occurs under stress cycling at such high stress levels. (4) Reduction of the fatigue strength due to localized hardening can be removed by introducing the cold working of the specimen surface after quenching.

本文言語English
ページ(範囲)308
ページ数1
ジャーナルNihon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A
67
654
DOI
出版ステータスPublished - 2001

ASJC Scopus subject areas

  • 材料科学(全般)
  • 材料力学
  • 機械工学

フィンガープリント

「Fatigue properties of steel with super rapid induction localized quenching」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル