Fracture Mode Transition and Miner's Law in Extremely Low Cycle Fatigue

Jun Komotori, Masao Shimizu

研究成果: Article査読

抄録

Low cycle fatigue tests and microcrack propagation tests were carried out under strain cycling with two-step variable plastic strain amplitude on annealed low carbon steel and commercial pure iron. The applicability of Miner's law to the extremely low cycle fatigue has been discussed in relation to the fracture mode transition and the damage accumulation mechanism in the extremely low cycle regime. It was found that the surface microcrack initiated at a low plastic strain ΔεP1 in low to high variable amplitude tests becomes nonpropagating at a high plastic strain ΔεP2 because of its blunting under large plastic strain, and that in such a situation, final failure occurs in a different fracture mode from the surface microcracking by the striation mechanism. The total fatigue life is controlled by the development of internal microvoid ahead of the crack in pure iron and by the initiation of an internal crack associated with the pearlite cracking in low carbon steel. In such a case, the damage accumulation does not occur linearly with strain cycling and the value of Σ ni/Nft becomes larger than unity.

本文言語English
ページ(範囲)1731-1734
ページ数4
ジャーナルTransactions of the Japan Society of Mechanical Engineers Series A
54
505
DOI
出版ステータスPublished - 1988 1 1
外部発表はい

ASJC Scopus subject areas

  • 材料科学(全般)
  • 材料力学
  • 機械工学

フィンガープリント

「Fracture Mode Transition and Miner's Law in Extremely Low Cycle Fatigue」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル