Observation and analysis of percolation behavior in carbon microcoils/silicone-rubber composite sheets

T. Katsuno, X. Chen, S. Yang, S. Motojima, M. Homma, T. Maeno, M. Konyo

研究成果: Article

27 引用 (Scopus)

抜粋

The electrical properties of carbon microcoils (CMCs)/ silicone-rubber composites were studied on the changes in the values of the electrical parameters (impedance, phase angle, resistance, and capacitance) as a function of the CMC content in the matrix, using an impedance analyzer in the frequency range from 40 to 200 kHz. Percolation paths were observed at a 3 wt % CMC content in the matrix. The properties of the composites were separated at the percolation threshold. The capacitance with a small value was dominant at CMC content less than 3 wt %, and the resistance was dominant at CMC content higher than 3 wt %.