Photoluminescence enhancement of ZnS:Mn2+ nanocrystal phosphors: Comparison of organic and inorganic surface modifications

Hayato Takahashi, Tetsuhiko Isobe

研究成果: Article査読

18 被引用数 (Scopus)


ZnS:Mn2+ nanocrystals of 3 nm in diameter were coated with silica to form 20 ± 4 nm core/shell particles, as observed by transmission electron spectroscopy. For ZnS:Mn2+ nanocrystals modified with silica, the intensity of photoluminescence (PL) due to the d-d transition of Mn2+ increases with increasing tetraethyl orthosilicate (TEOS) amount and hence with increasing the thickness of silica shell. This is attributed to the passivation of surface defects and the quantum confinement effect. On the contrary, the PL intensity of the ZnS:Mn 2+ nanocrystals modified by both lauryl phosphate (HLP) and silica decreases with increasing TEOS amount. 31P CP/MAS NMR spectroscopy reveals that the chemical interaction between phosphate groups and ZnS:Mn 2+ is interrupted by the silica shell. These results suggest that the surface modification of HLP around the ZnS:Mn2+ nanocrystals is more effective than the formation of the silica shell from the viewpoint of PL enhancement.

ジャーナルJapanese Journal of Applied Physics, Part 1: Regular Papers and Short Notes and Review Papers
出版ステータスPublished - 2005 2 1

ASJC Scopus subject areas

  • 工学(全般)
  • 物理学および天文学(全般)


「Photoluminescence enhancement of ZnS:Mn<sup>2+</sup> nanocrystal phosphors: Comparison of organic and inorganic surface modifications」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。