Point Defect Hardening in MgO·3Al2O3

Hisayuki Suematsu, Takayoshi Iseki, Toyohiko Yano, Yasutoshi Saito, Tetsuya Suzuki, Tsutomu Mori

研究成果: Article

28 引用 (Scopus)

抜粋

Vickers hardness in spinel increases by 23% after neutron irradiation to a fluence of 8.3 × 1022 n/m2 at 100°C. Annealing at high temperatures above 100°C gradually decreases the hardness. Above 500°C, the hardness is reduced to almost the same value as that of unirradiated material. The hardness of spinel, irradiated at 470°C to a fluence of 2.4 × 1024 n/m2, is unchanged both after irradiation and after annealing up to 1000°C. The length change during annealing was also measured and is similar to the hardness change. Frank dislocation loops with a density of 3 × 1014/cm3 are induced by neutron irradiation at 470°C but they apparently do not affect the hardening in spinel. Thus, point defects are concluded to act as obstacles against dislocation movement. The yield stress measured at 1400°C is also unchanged after irradiation. It is believed that not only the point defects but also the loops are annihilated by annealing at 1400°C.

元の言語English
ページ(範囲)1742-1747
ページ数6
ジャーナルJournal of the American Ceramic Society
75
発行部数7
DOI
出版物ステータスPublished - 1992
外部発表Yes

ASJC Scopus subject areas

  • Ceramics and Composites
  • Materials Chemistry

フィンガープリント Point Defect Hardening in MgO·3Al<sub>2</sub>O<sub>3</sub>' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用