Poly (Ricinoleic acid) based novel thermosetting elastomer

Hiroki Ebata, Mayumi Yasuda, Kazunobu Toshima, Shuichi Matsumura

研究成果: Article査読

25 被引用数 (Scopus)

抄録

A novel bio-based thermosetting elastomer was prepared by the lipase-catalyzed polymerization of methyl ricinoleate with subsequent vulcanization. Some mechanical properties of the cured carbon black-filled polyricinoleate compounds were evaluated as a thermosetting elastomer. It was found that the carbon black-filled polyricinoleate compounds were readily cured by sulfur curatives to produce a thermosetting elastomer that formed a rubber-like sheet with a smooth and non-sticky surface. The curing behaviors and mechanical properties were dependent on both the molecular weight of the polyricinoleate and the amount of the sulfur curatives. Cured compounds consisting of polyricinoleate with a molecular weight of 100,800 showed good mechanical properties, such as a hardness of 48 A based on the durometer A measurements, a tensile strength at break of 6.91 MPa and an elongation at break of 350%.

本文言語English
ページ(範囲)315-320
ページ数6
ジャーナルJournal of oleo science
57
6
DOI
出版ステータスPublished - 2008

ASJC Scopus subject areas

  • 化学 (全般)
  • 化学工学(全般)

フィンガープリント

「Poly (Ricinoleic acid) based novel thermosetting elastomer」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル