Superconductivity in AgxTaS2 single crystals with stage structure obtained via proton-driven ion introduction

Masaya Fujioka, Naoki Kubo, Masanori Nagao, Robin Msiska, Naoki Shirakawa, Satoshi Demura, Hideaki Sakata, Hideo Kaiju, Junji Nishii

研究成果: Article査読

3 被引用数 (Scopus)

抄録

Ag+ ions were intercalated into the transition-metal dichalcogenide TaS2 using the recently developed method of proton-driven ion introduction. Single-crystalline Ag0.58TaS2 with a stage 1 structure and Ag0.21TaS2 with a stage 2 structure were prepared using this method. The stage 2 structure of Ag0.21TaS2 was formed by exploiting the differences in ion diffusion properties among the polytypes of TaS2. Furthermore, our intercalation method can forcibly insert Ag+ ions into interlayers by applying a high voltage at low temperature (100°C), resulting in the formation of thermodynamically metastable phase. Such a synthesis approach offers a potential route for diversifying intercalation compounds with different stage structures. The first observations of superconductivity in AgxTaS2 were demonstrated in this study. The onset of superconductivity of AgxTaS2 was estimated to be 0.4 and 1.7 K in the samples with x = 0.58 and x = 0.21, respectively. Some anomalies, which were speculatively attributed to charge density wave order, were confirmed in the resistivity measurements of AgxTaS2. The results suggested that the anomalies were closely correlated with the superconducting transition temperature.

本文言語English
ページ(範囲)963-967
ページ数5
ジャーナルJournal of the Ceramic Society of Japan
126
12
DOI
出版ステータスPublished - 2018 12月
外部発表はい

ASJC Scopus subject areas

  • セラミックおよび複合材料
  • 化学 (全般)
  • 凝縮系物理学
  • 材料化学

フィンガープリント

「Superconductivity in AgxTaS2 single crystals with stage structure obtained via proton-driven ion introduction」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル