Synthesis and radical polymerization of perfluoro-2-methylene-1,3- dioxolanes

Weihong Liu, Yasuhiro Koike, Yoshi Okamoto

研究成果: Article

22 引用 (Scopus)

抜粋

A new efficient synthetic route was developed for perfluorinated 2-methylene-1,3-dioxolane monomers via a direct fluorination of the hydrocarbon precursors prepared from methyl pyruvate and diols. Perfluoro-2-methylene-4,5- dimethyl-1,3-dioxolane (PMDD) and perfluoro-3-methylene-2,4-dioxabicyclo-[4.3.0] nonane (PMDN) were thus synthesized via this new method, among which PMDN is first reported. The radical polymerizations of those monomers were performed under various conditions. The kinetic results indicated that polymerization rate of PMDD is higher than that of PMDN. Oxygen did not affect the polymerization yield but strongly affected the polymer structure. The polymerization in the presence of oxygen produced a polymer containing unstable units. Hydrogen-containing solvents result in a lower molecular weight polymer. 2,2′-Azobis(isobutyronitrile) cannot initiate the polymerization in a perfluoro solvent or in bulk. Also, photopolymerizations of those monomers were performed in the presence of carbon tetrabromide or carbon tetrachloride, and the mechanism is discussed. The polymer of PMDD has a glass transition temperature at 155 °C, and the polymer of PMDN has a glass transition temperature at 161 °C. These polymers with high glass transition temperature, low refractive index, low material dispersion, and extraordinary optical transmission from the deep ultraviolet to near-infrared regions may be used as optical fibers, pellicles, or antireflective coating materials.

元の言語English
ページ(範囲)9466-9473
ページ数8
ジャーナルMacromolecules
38
発行部数23
DOI
出版物ステータスPublished - 2005 11 15

ASJC Scopus subject areas

  • Organic Chemistry
  • Polymers and Plastics
  • Inorganic Chemistry
  • Materials Chemistry

フィンガープリント Synthesis and radical polymerization of perfluoro-2-methylene-1,3- dioxolanes' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用