Synthesis of blue-luminescent CaNb2O6 by using a biphasic liquid method at low temperatures

研究成果: Article

3 引用 (Scopus)

抜粋

We investigated a novel simple method to synthesize CaNb2O 6 from precursors formed in immiscible liquid-liquid biphasic systems. Niobium pentaethoxide and calcium acetate monohydrate were used as starting materials, which were dissolved separately in hexane and water, respectively. After putting the hexane solution on the aqueous solution, they started to react at the interface of the two liquid phases and then a mixture of calcium acetate and amorphous niobate gels was precipitated in the aqueous solution at room temperature. The precipitates could be transformed to CaNb 2O6 by heating at 700°C for 30min. The morphology of the CaNb2O6 sample was characterized as rough and dimpled spheres 400-500nm in size. The sample exhibited a blue emission upon excitation with ultraviolet light. A comparative study using a one-phase liquid method or a solid-state reaction method has strongly suggested that the biphasic liquid method is advantageous for obtaining highly luminescent CaNb2O 6 at the lower processing temperatures.

元の言語English
ページ(範囲)12-16
ページ数5
ジャーナルJournal of the Ceramic Society of Japan
122
発行部数1421
DOI
出版物ステータスPublished - 2014 1

ASJC Scopus subject areas

  • Ceramics and Composites
  • Chemistry(all)
  • Condensed Matter Physics
  • Materials Chemistry

フィンガープリント Synthesis of blue-luminescent CaNb<sub>2</sub>O<sub>6</sub> by using a biphasic liquid method at low temperatures' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用