Synthesis of perovskite Pb(Zn1/3Nb2/3)O3 powders via a polymer complex solution route with a large excess of polyethylene glycol

Wha Sup Lee, Tetsuhiko Isobe, Mamoru Senna

研究成果: Article査読

8 被引用数 (Scopus)

抄録

A polymer complex solution process was employed to produce perovskite Pb(Zn1/3Nb2/3)O3 (PZN) from a solution comprising Pb(NO3)2, ZnCl2, NbCl5 and polyethylene glycol (PEG). X-ray diffraction peaks due to the perovskite phase were observed after firing at temperatures between 700 and 1000°C. By increasing the concentration of PEG, the perovskite phase appeared at a lower temperature. With 600 vol% PEG and after heating at 800°C for 1 h, perovskite PZN amounted to 91% of the total solid product. The role of ligand-to-metal charge transfer during polymer complex formation on the apparent stabilization of PZN is discussed by using UV-VIS.

本文言語English
ページ(範囲)43-54
ページ数12
ジャーナルAdvanced Powder Technology
13
1
DOI
出版ステータスPublished - 2002 1 1

ASJC Scopus subject areas

  • Chemical Engineering(all)
  • Mechanics of Materials

フィンガープリント 「Synthesis of perovskite Pb(Zn<sub>1/3</sub>Nb<sub>2/3</sub>)O<sub>3</sub> powders via a polymer complex solution route with a large excess of polyethylene glycol」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル