Ultrahydrophobic silica films by sol-gel process

Sanjay S. Latthe, Hiroaki Imai, V. Ganesan, A. Venkateswara Rao

研究成果: Article

31 引用 (Scopus)

抄録

Wettability of solid surfaces is a crucial concern in our daily life as well as in engineering and science. The present research work describes the room temperature (27 °C) synthesis of adherent and water repellent silica films on glass substrates using vinyltrimethoxysilane (VTMS) as a hydrophobic reagent by a single step sol-gel process. The silica sol was prepared by keeping the molar ratio of tetraethoxysilane (TEOS), methanol (MeOH), water (H2O) constant at 1:14.69:5, respectively, with 0.01 M NH4F throughout the experiments and the VTMS/TEOS molar ratio (M) was varied from 0 to 0.97. The effects of M on the surface structure and hydrophobicity have been researched. The static water contact angle as high as 144° and water sliding angle as low as 14° was obtained for silica film prepared from M = 0.97. The hydrophobic silica films retained their hydrophobicity up to a temperature of 255 °C and above this temperature the films became superhydrophilic. The prepared silica films were characterized by Scanning Electron Microscopy (SEM), Atomic Force Microscopy (AFM), Fourier Transform Infrared (FT-IR) spectroscopy, humidity test and static and dynamic water contact angle measurements.

元の言語English
ページ(範囲)565-571
ページ数7
ジャーナルJournal of Porous Materials
17
発行部数5
DOI
出版物ステータスPublished - 2010 10

Fingerprint

Silicon Dioxide
Sol-gel process
Silica
Water
Hydrophobicity
Contact angle
Polymethyl Methacrylate
Polymers
Angle measurement
Sols
Surface structure
Temperature
Fourier transform infrared spectroscopy
Methanol
Wetting
Atomic force microscopy
Atmospheric humidity
Glass
Scanning electron microscopy
Substrates

ASJC Scopus subject areas

  • Mechanical Engineering
  • Mechanics of Materials
  • Materials Science(all)

これを引用

Ultrahydrophobic silica films by sol-gel process. / Latthe, Sanjay S.; Imai, Hiroaki; Ganesan, V.; Rao, A. Venkateswara.

:: Journal of Porous Materials, 巻 17, 番号 5, 10.2010, p. 565-571.

研究成果: Article

Latthe, Sanjay S. ; Imai, Hiroaki ; Ganesan, V. ; Rao, A. Venkateswara. / Ultrahydrophobic silica films by sol-gel process. :: Journal of Porous Materials. 2010 ; 巻 17, 番号 5. pp. 565-571.
@article{6b42e96e4f3c40acbe4bb94ff2814c26,
title = "Ultrahydrophobic silica films by sol-gel process",
abstract = "Wettability of solid surfaces is a crucial concern in our daily life as well as in engineering and science. The present research work describes the room temperature (27 °C) synthesis of adherent and water repellent silica films on glass substrates using vinyltrimethoxysilane (VTMS) as a hydrophobic reagent by a single step sol-gel process. The silica sol was prepared by keeping the molar ratio of tetraethoxysilane (TEOS), methanol (MeOH), water (H2O) constant at 1:14.69:5, respectively, with 0.01 M NH4F throughout the experiments and the VTMS/TEOS molar ratio (M) was varied from 0 to 0.97. The effects of M on the surface structure and hydrophobicity have been researched. The static water contact angle as high as 144° and water sliding angle as low as 14° was obtained for silica film prepared from M = 0.97. The hydrophobic silica films retained their hydrophobicity up to a temperature of 255 °C and above this temperature the films became superhydrophilic. The prepared silica films were characterized by Scanning Electron Microscopy (SEM), Atomic Force Microscopy (AFM), Fourier Transform Infrared (FT-IR) spectroscopy, humidity test and static and dynamic water contact angle measurements.",
keywords = "Adherent, Contact angle, Humidity, Hydrophobic, Sliding angle, Thermal stability",
author = "Latthe, {Sanjay S.} and Hiroaki Imai and V. Ganesan and Rao, {A. Venkateswara}",
year = "2010",
month = "10",
doi = "10.1007/s10934-009-9325-0",
language = "English",
volume = "17",
pages = "565--571",
journal = "Journal of Porous Materials",
issn = "1380-2224",
publisher = "Springer Netherlands",
number = "5",

}

TY - JOUR

T1 - Ultrahydrophobic silica films by sol-gel process

AU - Latthe, Sanjay S.

AU - Imai, Hiroaki

AU - Ganesan, V.

AU - Rao, A. Venkateswara

PY - 2010/10

Y1 - 2010/10

N2 - Wettability of solid surfaces is a crucial concern in our daily life as well as in engineering and science. The present research work describes the room temperature (27 °C) synthesis of adherent and water repellent silica films on glass substrates using vinyltrimethoxysilane (VTMS) as a hydrophobic reagent by a single step sol-gel process. The silica sol was prepared by keeping the molar ratio of tetraethoxysilane (TEOS), methanol (MeOH), water (H2O) constant at 1:14.69:5, respectively, with 0.01 M NH4F throughout the experiments and the VTMS/TEOS molar ratio (M) was varied from 0 to 0.97. The effects of M on the surface structure and hydrophobicity have been researched. The static water contact angle as high as 144° and water sliding angle as low as 14° was obtained for silica film prepared from M = 0.97. The hydrophobic silica films retained their hydrophobicity up to a temperature of 255 °C and above this temperature the films became superhydrophilic. The prepared silica films were characterized by Scanning Electron Microscopy (SEM), Atomic Force Microscopy (AFM), Fourier Transform Infrared (FT-IR) spectroscopy, humidity test and static and dynamic water contact angle measurements.

AB - Wettability of solid surfaces is a crucial concern in our daily life as well as in engineering and science. The present research work describes the room temperature (27 °C) synthesis of adherent and water repellent silica films on glass substrates using vinyltrimethoxysilane (VTMS) as a hydrophobic reagent by a single step sol-gel process. The silica sol was prepared by keeping the molar ratio of tetraethoxysilane (TEOS), methanol (MeOH), water (H2O) constant at 1:14.69:5, respectively, with 0.01 M NH4F throughout the experiments and the VTMS/TEOS molar ratio (M) was varied from 0 to 0.97. The effects of M on the surface structure and hydrophobicity have been researched. The static water contact angle as high as 144° and water sliding angle as low as 14° was obtained for silica film prepared from M = 0.97. The hydrophobic silica films retained their hydrophobicity up to a temperature of 255 °C and above this temperature the films became superhydrophilic. The prepared silica films were characterized by Scanning Electron Microscopy (SEM), Atomic Force Microscopy (AFM), Fourier Transform Infrared (FT-IR) spectroscopy, humidity test and static and dynamic water contact angle measurements.

KW - Adherent

KW - Contact angle

KW - Humidity

KW - Hydrophobic

KW - Sliding angle

KW - Thermal stability

UR - http://www.scopus.com/inward/record.url?scp=77955926466&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=77955926466&partnerID=8YFLogxK

U2 - 10.1007/s10934-009-9325-0

DO - 10.1007/s10934-009-9325-0

M3 - Article

AN - SCOPUS:77955926466

VL - 17

SP - 565

EP - 571

JO - Journal of Porous Materials

JF - Journal of Porous Materials

SN - 1380-2224

IS - 5

ER -