Water repellent porous silica films by sol-gel dip coating method

A. Venkateswara Rao, Annaso B. Gurav, Sanjay S. Latthe, Rajiv S. Vhatkar, Hiroaki Imai, Charles Kappenstein, P. B. Wagh, Satish C. Gupta

研究成果: Article査読

67 被引用数 (Scopus)

抄録

The wetting of solid surfaces by water droplets is ubiquitous in our daily lives as well as in industrial processes. In the present research work, water repellent porous silica films are prepared on glass substrate at room temperature by sol-gel process. The coating sol was prepared by keeping the molar ratio of methyltriethoxysilane (MTES), methanol (MeOH), water (H2O) constant at 1:12.90:4.74, respectively, with 2M NH4OH throughout the experiments and the molar ratio (M) of MTES/Ph-TMS was varied from 0 to 0.22. A simple dip coating technique is adopted to coat silica films on the glass substrates. The static water contact angle as high as 164° and water sliding angle as low as 4° was obtained for silica film prepared from M=0.22. The surface morphological studies of the prepared silica film showed the porous structure with pore sizes typically ranging from 200nm to 1.3μm. The superhydrophobic silica films prepared from M=0.22 retained their superhydrophobicity up to a temperature of 285°C and above this temperature the films became superhydrophilic. The porous and water repellent silica films are prepared by proper alteration of the Ph-TMS in the coating solution. The prepared silica films were characterized by surface profilometer, scanning electron microscopy (SEM), transmission electron microscopy (TEM), Fourier Transform Infrared (FT-IR) spectroscopy, humidity tests, chemical aging tests, static and dynamic water contact angle measurements.

本文言語English
ページ(範囲)30-35
ページ数6
ジャーナルJournal of Colloid And Interface Science
352
1
DOI
出版ステータスPublished - 2010 12 1

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Biomaterials
  • Surfaces, Coatings and Films
  • Colloid and Surface Chemistry

フィンガープリント 「Water repellent porous silica films by sol-gel dip coating method」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル